水凝胶电解质的协同化学和界面工程增强固态锌空气电池的耐久性( 三 )



IOSHs-NSC-Co9S8
interdigital
Alkaline PAM-co-PAA with  6 m KOH and 0.2 m  Zn(Ac)2
1.408 V
738? mAh g?1
60? mW cm?2
35?h 5 mA cm?2
Charging and discharging curves  remained unchanged under different bending angles of 30° 45° 90° and 180°

CNT sheets
Fiber
Alkaline PVA and PEO with KOH
N.A.
6 Ah L?1
(0.99 mW cm?2) 5.7 Wh L?1
30 h 1 mA g?1
Discharge voltage remained  almost unchanged before and after: i) bending to 120° for 100 cycles; ii)  stretching by 10%